CMXBM- Martensitic Stainless Steel

Steel data sheets

Choose the measure unit in which display the data:

Valbruna Grade

CMXBM

Steel type

Martensitic Stainless Steel

Description of material

CMXBM is a high Carbon martensitic stainless steel with specific Mo-V contents designed to supply high hardness. Its corrosion resistance cannot be as good as Chromium 18% grades due to the high Carbon content. Because of its high hardness after heat treatment, CMXBM is used in applications where this characteristic is the most important. Its Molybdenum and Vanadium contents are higher, and with more stable Carbides, than CMXC and CMXC1 but other properties and characteristics are substantially the same.

Applications

All applications where high hardness is indispensable such as bearing balls, fuel injection needles, valve seats, parts of pumps, wear resistant devices and professional cutlery (not table cutlery). CMXBM is widely used in fuel injection devices in automotive industries.

Melting practices

EAF+AOD

Corrosion resistance

CMXBM has its maximum corrosion resistance when in the hardened + low temperature tempered condition and with its maximum hardness. Its use in the annealed condition or any other situation able to reduce the surface hardness and in environments containing Chloride, should be avoided. CMXBM has good corrosion resistance in mild environments such as fresh water, industrial and rural atmospheres, petroleum products, gasoline fuel oil and alcohol. It should be noted that this grade, as for every kind of stainless steel, surfaces should be free of contaminant and scale, heat tint, and passivated for optimum resistance to corrosion.

Cold working

In the annealed condition, CMXBM is not suitable for cold forming operations such as cold heading or up-setting. Nevertheless, a moderate cold formability could be obtained after a long lasting annealing and very slow cooling in furnace. It should be pointed out that CMXBM is prone to surface decarburization: a protective atmosphere should be considered in the heat treatment of finished pieces.

Machinability

In the annealed condition CMXBM has a good machinability due its micro-sulphurizing and is better than the CMX series whose Sulphur content is very low. CMXBM offers significant advantages in terms of machining cost saving in fuel injection production. However, it’s important to know that the productivity gain depends on the type of machines used, the kind of tools used and their geometry, cutting fluids and the kind of machine operations on the pieces produced. Grinding and polishing of hardened + tempered material at maximum values of hardness must be carried out with great care in order to avoid the overheating of the surface of the piece resulting in poor corrosion resistance and/or grinding cracks.

Weldability

This process is very risky and shouldn’t be a cycle of production to apply. Different and alternative choices should be evaluated to join parts. In any case, if welding process were required, a preheating is mandatory and the part must be maintained at temperature and followed by immediate annealing. Fillers of the same composition can be used to obtain mechanical properties close to that of the base metal. Alternatively, austenitic fillers may be used considering an inevitable reduction of these properties.

Hot working

Blooms and ingots require a suitable preheating to avoid cracks and a slow cooling in furnace after forging. Overheating must always avoided in order to reduces the risk of internal bursts. An improper cooling could result in stress cooling cracks. Large forgings and large cross – section shapes should be left to cool until their core reaches room temperature and, then, immediately heat treated. A right and suitable heat treatment of pieces after forging process creates a structure with no or little retained austenite avoiding delayed cracks.

Heat treatment

CMXBM should be double tempered after hardening in order to reduce or avoid retained austenite obtaining high values of hardness. Alternatively, a cryogenic treatment after hardening and tempering can be carried out but this must always be followed by another tempering.

Designations

W.N. 1.4112
EN X90CrMoV18